3. ResultsThe average AFM topographic data and mass loss corrosion rate are presented in Table 2 for all steels, timepoints, and fluids. The mass loss corrosion rate was calculated at each time point following the form given by Mundhenk et al. (2013) [6]. If the change in mass was not measurable (i.e., below the LOD), the corrosion rate was incalculable; this does not necessarily mean that zero corrosion occurred, however.